C12000 Phosphorus Deoxidized Copper
- Classification & Chemical Composition
|
Classification
|
UNS
|
Chemical Composition
|
|
DUNS Nr.
|
Shape
|
Cu
|
P
|
|
C1201
|
Plate
|
C1201P
|
≥ 99.90
|
"0.004~0.015"
|
|
Rod
|
C1201R
|
|
C1220
|
Plate
|
C1220P
|
≥ 99.90
|
"0.015~0.040"
|
|
Rod
|
C1220P
|
|
C1221
|
Plate
|
C1221P
|
≥ 99.75
|
"0.004~0.040"
|
|
Rod
|
C1221P
|
 |
- Melting Point: 1083°C
- Hot Temperature Range:
750°C ~ 875°C
- Annealing Temperature Range:
375°C ~ 650°C
- Machinability: 20% of Brass |
|
DUNS
Nr.
|
Temper
|
Description
|
Tensile Test
|
Bending Test
|
Hardness Test
|
|
T (mm)
|
Strength
(N/㎜²)
|
Elongation (%)
|
T (mm)
|
Angle
|
Inner “R”
|
T (mm)
|
HV
|
|
C1201
C1220
C1221
|
O
|
C1201P-O
|
0.3~30
|
≥ 195
|
≥ 35%
|
≤ 2
|
180°
|
-
|
-
|
-
|
|
C1220P-O
|
|
C1221P-O
|
|
C1201R-O
|
0.3~3
|
|
C1220R-O
|
|
C1221R-O
|
|
1/4H
|
C1201P-1/4H
|
0.3~30
|
215~275
|
≥ 25%
|
≤ 2
|
180°
|
"T X 0.5"
|
0.3 이상
|
55~100
|
|
C1220P-1/4H
|
|
C1221P-1/4H
|
|
C1201R-1/4H
|
0.3~3
|
|
C1220R-1/4H
|
|
C1221R-1/4H
|
|
1/2H
|
C1201P-1/2H
|
0.3~20
|
245~315
|
≥ 15%
|
≤ 2
|
180°
|
"T X 1.0"
|
0.2 이상
|
75~120
|
|
C1220P-1/2H
|
|
C1221P-1/2H
|
|
C1201R-1/2H
|
0.3~3
|
|
C1220R-1/2H
|
|
C1221R-1/2H
|
|
H
|
C1201P-H
|
0.3~10
|
≥ 275
|
-
|
≤ 2
|
180°
|
"T X 1.5"
|
≥ 0.2
|
≥ 80
|
|
C1220P-H
|
|
C1221P-H
|
|
C1201R-H
|
0.3~30
|
|
C1220R-H
|
|
C1221R-H
|
-Electrical, thermal conductivity, drawing formability and corrosion resistance is good
-C1220 is free from hydrogen embrittlement heated at elevated temperature in reducing atmosphere
-C1201 is superior to C1220 and C1221 for Electrical Conductivity.
- Automobile Parts: Radiator Pin and Gasket
- Construction Parts: Copper Roof shield and Boiler
- Kitchen Parts: Dishes and Bowls
- Air Conditioner: Cold Air Conditioner and Panels